Researchers Optimize Thermoelectric Properties of Lead Telluride Material Systems

In a recent study, a research team from the Hefei Institutes of Physical Science of the Chinese Academy of Sciences achieved higher thermoelectric performance of n-type lead telluride (PbTe) by adjusting the band structure and enhancing phonon scattering.

Results were published in Nanoscale.

"We have increased the material power factor and decreased thermal conductivity," said Prf. QIN Xiaoying, who led the team.

PbTe is one of the most promising medium-temperature thermoelectric materials. However, n-type PbTe materials have a lower thermoelectric figure of merit compared to p-type PbTe materials. This is mainly due to the large energy shift between the light and heavy bands in PbTe conduction band, which makes it difficult to achieve energy band simplification in n-type PbTe, resulting in a lower power factor. Therefore, more in-depth and systematic studies are needed to effectively and significantly improve the thermoelectric performance of n-type PbTe.

Now, the researchers constructed the Pb_0.97Sb_0.03Te + y wt. % Cu₁₂Sb₄S₁₃(y=0,1.25,1.5,1.75) composite system. This was achieved by doping the PbTe matrix with antimony (Sb) elements and introducing a small amount of Cu₁₂Sb₄S₁₃ nanoparticles. Thy also used the in-situ reaction to construct a semi-coherent nanophase.

This study focuses on optimizing the carrier concentration in n-type PbTe using host element doping, while combining energy band engineering/energy filtering effects to improve its electrical properties.

On this basis, in situ reactions were used to construct semi-coherent nanophases and introduce multi-scale defects to scatter phonons. This allowed them to improve the power factor, reduce thermal conductivity, and thus increase thermoelectric figure of merit (ZT).

They found that the composite sample Pb_0.97Sb_0.03Te + 1.5 wt. % Cu₁₂Sb₄S₁₃ had excellent thermoelectric properties with a ZT of 1.58 (773 K), an improvement of about 75% compared with Pb_0.97Sb_0.03Te.

This work proved the incorporation of Cu₁₂Sb₄S₁₃ nanoparticles was an effective way to improve the thermoelectric properties of Pb_0.97Sb_0.03Te, which was of great importance for the study of the regulation of the thermoelectric properties of n-type PbTe.

This work was supported by the National Natural Science Foundation of China, the Natural Science Foundation of Anhui Province, and the President's Fund of the Hefei Institute of Physics.